Common problems and analysis of composite runway construction.

Release date:2018-04-16 Author: Click:

复合塑胶跑道


Common problems and analysis on construction of composite plastic runway:


1. Plastic drum, and basic detachment phenomenon.

After finishing, the plastic layer will appear local or large area in a short time, or it will be separated from the base.

Reason analysis:

The cement label is not qualified or the basic insulation layer is not qualified, the underground water gas rises, the plastic layer is raised, causing the plastic layer to appear the drum phenomenon.

Treatment measures:

Cut off the bubbling part, dry the base to make the waterproof treatment, then press the requirement to fill, then the color difference.

Preventive measures:

The basic moisture content and the air humidity should be within the safe range.

2. Drum of plastic layer.

Reason analysis:

During construction, the base moisture content is high, or the air humidity is high, or the slurry water is high, or the diluent is high, resulting in the reaction of the isocyanate root in pu materials, producing carbon dioxide. When the plastic material reaches a certain strength, the carbon dioxide cannot spread to the outside of the material completely, and gradually accumulates inside the material, causing a blister on the surface of the plastic surface.

Treatment measures:

Cut off the bubbling part, dry the base to make the waterproof treatment, then press the requirement to fill, then the color difference.

Preventive measures:

The basic moisture content and air humidity should be in the safe range. Before construction, we should make a small test.

3. The product has not been cured after the curing period, and there is no big reason for strength or viscosity:

(1) during construction, the material proportion error exceeds the safety range, resulting in the imbalance of component proportion, resulting in the material not producing crosslinking reaction, so that the material is too viscous and not even strong.

(2) no catalyst, too little catalyst dose or failure of catalyst. These three aspects will cause the material to be unable to react completely, affecting the strength of the material.

(3) the diluent is not qualified and contains other impurities, such as alcohol, water, etc., causing the molecular chain to be blocked in the reaction of the plastic material, unable to form the polymer, or causing the imbalance of proportion.


URL of this article:http://en./news/450.html

Related tags:复合塑胶跑道

最近浏览:

Message
name:
phone:
content:
Contact

Telephone:0535-6397288

Fax:0535-6385688

purchase ingredients:0535-3459802

Project contract:0535-6397288

Address:Yantai Development Zone Zhujiang Road No. 32

Web site:www.

Mailbox:sunny365@

Code

英文站底部二维码.png

Copyright 2018,Yantai Sunshine Plastic Co., Ltd. official website case number:    Internet planning:
s
e
r
v
i
c
e
二维码

Scan QR code

share 一键分享